Product Parameters of 7075 aluminum round tube:
Alloy grade
|
7075
|
Temper
|
O, T5, T6, T651, T7351 |
Outer diameter
|
10mm-500mm, or as per request |
Wall thickness |
As per request |
Length
|
≦12m |
Composition of 7075 T6 aluminum tube
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Zr |
Other |
AL |
0.4 |
0.5 |
1.2-2.0 |
0.3 |
2.1-2.9 |
0.3 |
2.1-2.9 |
0.18-0.28 |
- |
0.15 |
rest |
Mechanical Properties for 7075 aluminum tube:
Grade |
Thermal expansion coefficient (20-100℃) μm/m·k Rm/Mpa |
Melting point rane (℃) Rp0.2/Mpa |
Conductivity 20℃(68℉) Rp0.2/Mpa (%IACS) |
Resistivity 20℃(68℉) Ωmm2/m |
Density (20℃)(g/cm3) Ωmm2/m |
7075 T6 |
23.5 |
475-635 |
33 |
0.0515 |
2.9 |
Quality Chracoristics of 7075:
Density: 2.90g/cm³.
Shear strength: alloy (bare) and clad aluminum alloy, O state: 152MPa (22ksi); alloy (bare) T6, T7451 state: 331MPa (48ksi); clad aluminum alloy T6, T7451 state: 317MPa (46ksi)
Hardness: O state: 60HB; T6, T651 state: 150HB;
The data is taken from the test results of a 10mm diameter ball and 30s under a load of 500kg.
Poisson's ratio: 0.33.
Elastic modulus: Tension: 71.0GPa (10.3×106psi), Shear: 26.9GPa (3.9×106psi), compression 72.4GPa (10.5×106psi)
Fatigue strength: T6, T7451, T73 state: smooth and unnotched specimens are cycled 5×108 times in the R·R·Moore type test, which is 159MPa (23ksi)
Excet 7075, we also have aluminum tube made of other available alloy:
1xxx series: 1060,1070
2xxx series: 2024 T3, 2024 T4, 2024 T351
3xxx series: 3003 H32, 3A21 O, etc.
5xxx series: 5052, 5083,etc
6xxx series: 6061, 6063, 6005, 6060, etc
7xxx series: 7005,7050, etc